3D Pro Multilayer

HOME > 3D Pro
3D Pro Multilayer
3D Pro Multi Layered Zirconia is focused on multilayer ceramic restorations with Bloomden fabrications on esthetic dentistry. The innovative multi layered technology offering the best possible solution that meets the full arch requirements of the individual clinical esthetic expectation.
42%~49% Translucent
3Y-TZP+4Y-TZP+5Y-TZP
  • Indications

    indication.png

  • Benefits
  • Technical data
  • Chemical composition
    Component
    3D Pro
    ZrO2+HfO2+Y2O3≥99%
    Y2O34.5%-10%
    Al2O3<0.15%
    Other Oxides<0.5%



    <0.25%


  • Video tutorial
  • Brochures

Excellent Aesthetics

It is important to reproduce the translucency of the natural tooth, as it provides an enchanted natural appearance of the prosthetics. Translucency is the substance property that allows the passage of light and its dispersion, and then the objects will not be seen clearly through the material. This property could be defined as a state between transparency and complete opacity. Translucency can be regulated by controlling the absorption, reflection, and transmission of light through the material. The translucency is higher when the reluctance is low and the transmission is high.

image.png



Strength as a trend

Previously at very initial phase, the advancement in aesthetics was limited to the lower strength zirconia, such circumstance that couldn't enable technicians to use for bridges over 3 crowns. However Bloomden 3D Pro multilayer zirconia is unlike any other zirconia, it can exhibit a strength range from 650MPa to 1200MPa which can cover posteriors and anteriors for both crowns 

and bridges including implant restorations. The high strength layer (dentin layer) of 3D Pro is developed to avoid any areas of weakness when contacting food, or human's natural teeth.

image.png



Monoclinic resistance

3D Pro multilayer zirconia's unique hydrolysis microstructure and chemical formulation by the hydrothermal treatment also resist degradation of aging which the cubic shifted to monoclinic state that can be observed in zirconia structure.

image.png


High speed sintering cycle

one of 3D Pro multilayer zirconia's excellent attributes is the fast sintering cycle which can ensure the strength, translucency and aging resistance simultaneously. The high-productivity

sintering cycle allows for “inside furnace” time in 45 minutes.


image.png


Low Wear Rate

The average crystalline size of less than 0.5 μm and the Hydrolyzed powder properties are organized inside 3D Pro multilayer zirconia which enable 3D Pro multilayer zirconia to be long-term enamel wear behavior closed to the natural human teeth after several times of lab-test. The study revealed that the aged zirconia and polished zirconia both have identical roughness and less wear of opposing enamel.

image.png



Bloomzir® 3D Pro Multilayer is a combination of 3Y, 4Y and 5Y. 

For 5Y-TZP, it is 10% Y2O3, tetragonal 50%, Cube 50%, high translucent in the incisal phase 650MPa; 

For 3Y-TZP, it is 4.5% Y2O3, tetragonal 70%, Cube 30%, stablized zirconia in the dentin phase 1200MPa.

3D-pro-thickness.jpg

Bloomzir® 3D Pro Multilayer  Shade Range: VITA® 16 shades + 4 bleach shades (BL1, BL2, BL3, BL4)

image.png


Bloomzir® 3D Pro Multilayer  sintering illurstration:

1. Room temperature to 900°C (1652°F),  5°C/min, approximately by 180mins.

2. 900°C (1652°F) to 1500°C (2732°F), 8°C/min, approximately by 60mins.

3. Holding 1500°C (2732°F) for 120mins. 

4. Dropping from 1500°C (2732°F) to 900°C (1652°F), 5°C/min, approximately by 120mins.

3D烧结曲线.png

5. Natural cooling


Below is Bloomzir® 3D Pro Multilayer case:

Bloomzir® 3D Pro combined the concept of nature and beauty, with smooth color gradation, very matching VITA® shades as below full arch case shows. Meanwhile the Bloomzir® 3D Pro Multilayer phisical states can be kept well with our R&D technology to ensure a long term aesthetic apprearance.

below Video of Bloomzir® 3D Prshade A2 case: